Abstract
An unceasing scientific challenge to monitor the emissions of toxic and flammable gases in a selective approach is of great importance for safety of human health. As a result, herein, we report on the detailed study of the gas sensing characteristics of ZnO nanostructures prepared at various reaction pH and times. The findings revealed that the variation of synthesis reaction pH and times play a vital role on the morphology and structure. The [email protected] pH based sensor demonstrated a low response when exposed to reducing gases (CO, CH 4 and NH 3 ), volatile organic compounds (ethanol, acetone, benzene and toluene) and oxidizing gas (NO 2 ), while exposed to H 2 S gas unpreceded and reproducible response (i.e. 3 times more than the interfering gases) at low operating temperature of 75 °C was observed. The exceptional response (i.e. resistance ratio) observed at the low operating temperature towards 40 ppm H 2 S was elucidated by the improved gas accessibility and relative concentration of V O induced by structural transformation, which induced change in oxygen adsorption. The high H 2 S gas selectivity was ascribed to the reactivity of H 2 S and low temperature decomposition to participate in a reaction with a ZnO nanoplatelets-based sensor. The fundamental gas-sensing mechanism associated to the ZnO response and point defects at low operating temperature is evaluated in detail.
Original language | English |
---|---|
Pages (from-to) | 2189-2201 |
Number of pages | 13 |
Journal | Results in Physics |
Volume | 12 |
DOIs | |
Publication status | Published - Mar 2019 |
Keywords
- Gas sensing
- H S selectivity
- Point defects
- ZnO nanoplatelets
ASJC Scopus subject areas
- General Physics and Astronomy