Corrosion and Wear Behaviour of Spark Plasma-Sintered NiCrCoAlTiW-Ta Superalloy

Olugbenga Ogunbiyi, Tamba Jamiru, Rotimi Sadiku, Lodewyk Beneke, Oluwagbenga Adesina, Babatunde Abiodun Obadele

Research output: Contribution to journalArticlepeer-review

19 Citations (Scopus)


NiCrCoAlTiW-Ta superalloy was sintered using spark plasma sintering technique. The influence of starting powder particle size on the corrosion and dry sliding wear behaviour of sintered NiCrCoAlTiW-Ta superalloy was investigated. The nickel matrix (> 60 wt%) was varied over three different particle sizes (3–44, 45–106 and 106–150 µm). The powders were sintered at 1100 °C, heating rate of 100 °C/min and pressure of 32 MPa. The effect of particle sizes on sintered density, microhardness, corrosion and wear were reported. The results show that the sintered density of 97.48% and microhardness value of 382.88 HV0.1 were reported for the smallest starting powder. Furthermore, the microstructures of the sintered alloy revealed the presence of three major phases: γ, γ′ and the precipitated solid solution phase. There was an improvement in the corrosion response in relation to the particle size of the starting powder. This indicates that the least corrosive alloy has the least starting powder particle size. It has a corrosion rate of 0.047 and 0.056 mm/year in saline and acidic media, respectively. Also, the coefficient of friction increased with increase in powder particle size. However, the poor wear response of the alloys with bigger powder particle size could be attributed to poor adhesion of the oxide layer.

Original languageEnglish
Article number1
JournalJournal of Bio- and Tribo-Corrosion
Issue number1
Publication statusPublished - 1 Mar 2020


  • Corrosion
  • Particle size
  • Spark plasma sintering
  • Superalloy
  • Wear

ASJC Scopus subject areas

  • Materials Science (miscellaneous)
  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry


Dive into the research topics of 'Corrosion and Wear Behaviour of Spark Plasma-Sintered NiCrCoAlTiW-Ta Superalloy'. Together they form a unique fingerprint.

Cite this