Chitosan-based nanocomposites for de-nitrification of water

Novel chitosan (CTs) nanocomposite beads containing alumina (Al₂O₃, denoted as Al in the nanocomposites) and functionalized multiwalled carbon nanotubes (f-MWCNTs) (CTsAl/f-MWCNTs) were prepared using an environmentally benign phase inversion method and subsequently used for the removal of nitrates (NO₃ ⁻) in water. The ellipsoidal beads with an average size of 3 mm were readily formed at room temperature and contained a small amount of Al (20 wt%) and f-MWCNTs (5%). The beads were found to adsorb nitrates effectively over a wide range of pH (pH 2 – pH 6) and showed maximum nitrates removal of 96.8% from a 50 mg/L nitrate water solution. Pure CTs beads on the other hand removed only 23% at pH 4. Kinetic studies suggested that the particle diffusion was rate controlling step for the adsorption of nitrates on CTsAl/f-MWCNT nanocomposite beads. Langmuir-Freundlich isotherms revealed that the adsorption of nitrates was on the heterogeneous surface of CTsAl/f-MWCNT beads. The Dubinin–Radushkevich (D-R) isotherm further revealed that the adsorption of nitrates was by electrostatic interaction. Thermodynamic studies suggested that the adsorption was spontaneous and exothermic. More than 70% recovery was achieved for 5 cycles of desorption-degeneration studies. Al and f-MWCNTs have shown to improve swelling and solubility of CTs.